Hu, X., Guan, P., & Yan, X. (2004). Hydrothermal synthesis of nano-meter microporous zinc ferrite. China Particuology, 2(3), 135-137. https://doi.org/10.1016/S1672-2515(07)60040-2

Hydrothermal synthesis of nano-meter microporous zinc ferrite

Xiaoling Hu ^*, Ping Guan, Xin Yan

Department of Applied Chemistry, School of Science, Northwestern Polytechnic University, Xi'an 710072, P. R. China

10.1016/S1672-2515(07)60040-2

Volume 2, Issue 3, June 2004, Pages 135-137

Received 27 April 2004, Accepted 24 May 2004, Available online 27 November 2007.

E-mail: HuXL@nwpu.edu.cn

Highlights

Abstract

Nano-meter microporous zinc ferrite was prepared by a hydrothermal method, using triethylamine as a template. Adsorption curves showed that the product had a microporous structure. The effects of precursor pH, reaction temperature and reaction time on the preparation were studied, yielding optimal conditions: pH=11, 448 K, 360 min. The morphology of zinc ferrite as observed by TEM, showed that zinc ferrite was well-crystallized and well-dispersed with little conglomeration.